PRODUCT DATA SHEETProduct Number: 61474
Test
Methods
Notched 1/8" (3.2 mm)
Unnotched 1/8" (3.2 mm)
MIL B-81705C
4046.1
230 ºF @ 66 psi
110 ºC @ 455 kPa
D-648
|
PRODUCT DATA SHEET |
Material Type: Polycarbonate Product Number: 61474 |
||
|---|---|---|---|
| Processing Data | English Values | Metric Values | ASTM Test Methods |
| Injection pressure | 10,000-20,000 psi | 69-138 MPa | |
| Melt Temperature | 430-480 ºF | 221-249 ºC | |
| Mold Temperature | 125-200 ºF | 52-93 ºC | |
| Material Drying | 4 hrs @ 250 ºF | 4 hrs @ 121 ºC | |
| Dew Point | - 20 ºF | - 29 ºC | |
| Moisture Content | < 0.02% | <0.02% | |
| Physical | |||
| Specific Gravity | 1.19 | 1.19 | D-792 |
| Mold Shrinkage, 1/8" (3.2mm) | 0.006-0.009 in/in | 0.6-0.9 % | D-955 |
| Mechanical | |||
| Impact Strength, Notched 1/8" (3.2 mm) |
12.0 ft lbs/in | 641 J/m | D-256 |
| Impact Strength, Unnotched 1/8" (3.2 mm) |
30.0 ft lbs/in | 1602 J/m | D-256 |
| Tensile Strength | 7,000 psi | 48 MPa | D-638 |
| Tensile Elongation % | 10 + | 10 + | D-638 |
| Tensile Modulus | 0.24 x 106 psi | 1654 MPa | D-638 |
| Flexural Strength | 9,500 psi | 65 MPa | D-790 |
| Flexural Modulus | 0.26 x 106 psi | 1791 MPa | D-790 |
| Electrical | |||
| Volume Resistivity | 1011 | 1011 | D-257 |
| Surface Resistivity | 1011 | 1011 | D-257 |
| Static Decay, MIL B-81705C | < 2 seconds | < 2 seconds | FTMS 4046.1 |
| Thermal | |||
| Deflection Temperature | 220 ºF @ 264 psi 230 ºF @ 66 psi |
104 ºC @ 1820 kPa 110 ºC @ 455 kPa | D-648 |
| Flammability | V-2 | V-2 | UL 94 |
| Note: Data has been obtained from specimens molded under carefully controlled conditions and represents average values. Properties may vary or may be affected by molding conditions. No assurance can be implied that molded articles will have the same properties stated above. James R. Skinner & Co. ©1999 email: jrsco@idptech.com | |||