PRODUCT DATA SHEETProduct Number: 69558
Test
Methods
Notched 1/8" (3.2 mm)
Unnotched 1/8" (3.2 mm)
MIL B-81705C
4046.1
190 ºF @ 66 psi
88 ºC @ 455 kPa
D-648
|
PRODUCT DATA SHEET |
Material Type: ABS Product Number: 69558 |
||
|---|---|---|---|
| Processing Data | English Values | Metric Values | ASTM Test Methods |
| Injection pressure | 10,000-20,000 psi | 69-138 MPa | |
| Melt Temperature | 390-450ºF | 199-232 ºC | |
| Mold Temperature | 150-200 ºF | 66-93 ºC | |
| Material Drying | 2 hrs @ 180 ºF | 2 hrs @ 82 ºC | |
| Dew Point | 0 ºF | - 18 ºC | |
| Moisture Content | < 0.1% | <0.1% | |
| Physical | |||
| Specific Gravity | 1.06 | 1.06 | D-792 |
| Mold Shrinkage, 1/8" (3.2mm) | 0.0065-0.0075 in/in | 0.65-0.75 % | D-955 |
| Mechanical | |||
| Impact Strength, Notched 1/8" (3.2 mm) |
4.5 ft lbs/in | 240 J/m | D-256 |
| Impact Strength, Unnotched 1/8" (3.2 mm) |
30.0 ft lbs/in | 1602 J/m | D-256 |
| Tensile Strength | 5,400 psi | 37 MPa | D-638 |
| Tensile Elongation % | 8-10 | 8-10 | D-638 |
| Tensile Modulus | 0.30 x 106 psi | 2067 MPa | D-638 |
| Flexural Strength | 8,700 psi | 60 MPa | D-790 |
| Flexural Modulus | 0.28 x 106 psi | 1929 MPa | D-790 |
| Electrical | |||
| Volume Resistivity | 1010 | 1010 | D-257 |
| Surface Resistivity | 1011 | 1011 | D-257 |
| Static Decay, MIL B-81705C | < 2 seconds | < 2 seconds | FTMS 4046.1 |
| Thermal | |||
| Deflection Temperature | 160 ºF @ 264 psi 190 ºF @ 66 psi |
71 ºC @ 1820 kPa 88 ºC @ 455 kPa | D-648 |
| Flammability | HB | HB | UL 94 |
| Note: Data has been obtained from specimens molded under carefully controlled conditions and represents average values. Properties may vary or may be affected by molding conditions. No assurance can be implied that molded articles will have the same properties stated above. James R. Skinner & Co. ©1999 email: jrsco@idptech.com | |||